PC/ABS AC2500 020A FCFC TAIWAN
TAIRILOY®
Electrical field、Electronic field、Automotive sector
standard、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | FCFC TAIWAN/AC2500 020A |
|---|---|---|---|
| Rockwell hardness | R 计秤, 23°C | ISO 2039-2 | 114 |
| R 级, 23°C | ASTM D785 | 114 |
| Mechanical properties | Test Condition | Test Method | FCFC TAIWAN/AC2500 020A |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 93.0 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 2450 Mpa |
| tensile strength | 23°C | ASTM D638 | 54.0 Mpa |
| flammability | Test Condition | Test Method | FCFC TAIWAN/AC2500 020A |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | FCFC TAIWAN/AC2500 020A |
|---|---|---|---|
| Shrinkage rate | 流动 : 3.20 mm | ASTM D955 | 0.40 - 0.60 % |
| melt mass-flow rate | 240°C/5.0 kg | ASTM D1238 | 8.0 g/10 min |
| Shrinkage rate | 3.20 mm | ISO 2577 | 0.40 - 0.60 % |
| Thermal performance | Test Condition | Test Method | FCFC TAIWAN/AC2500 020A |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火, 6.35 mm，HDT | ASTM D648 | 106 °C |
| injection | Test Condition | Test Method | FCFC TAIWAN/AC2500 020A |
|---|---|---|---|
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 240 to 270 °C | ||
| Temperature at the rear of the barrel | 220 to 250 °C | ||
| Processing (melt) temperature | 250 to 270 °C | ||
| Hopper temperature | 60 to 80 °C | ||
| drying temperature | 100 to 110 °C | ||
| Temperature at the front of the material cylinder | 240 to 270 °C | ||
| Back pressure | 0.345 to 0.689 Mpa | ||
| Temperature | 70 to 90 °C | ||
| Spray nozzle temperature | 230 to 270 °C |