Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HDPE EQUATE PE EGDA-6888 EQUATE KUWAIT
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | EQUATE KUWAIT/EQUATE PE EGDA-6888 |
|---|---|---|---|
| Secant modulus | 1%正割,MD:15µm,吹塑薄膜 | ASTM D882 | 1220 MPa |
| tensile strength | TD:断裂,15µm,吹塑薄膜 | ASTM D882 | 57.0 MPa |
| Elmendorf tear strength | MD:15.0µm | ASTM D1922 | 70.0 kN/m |
| TD:15.0µm | ASTM D1922 | 150.0 kN/m | |
| Secant modulus | 1%正割,TD:15µm,吹塑薄膜 | ASTM D882 | 1470 MPa |
| film thickness | 15 µm | ||
| elongation | MD:断裂,15µm,吹塑薄膜 | ASTM D882 | 380 % |
| tensile strength | MD:断裂,15µm,吹塑薄膜 | ASTM D882 | 60.0 MPa |
| elongation | TD:断裂,15µm,吹塑薄膜 | ASTM D882 | 550 % |
| Dart impact | 15µm,吹塑薄膜 | ASTM D1709A | 170 g |
| physical property | Test Condition | Test Method | EQUATE KUWAIT/EQUATE PE EGDA-6888 |
|---|---|---|---|
| melt mass-flow rate | 190°C/21.6kg | ASTM D1238 | 10 g/10min |
| density | ASTM D792 | 0.952 g/cm³ | |
| Apparent density | ASTM D1895 | 560 kg/m³ |
| Thermal performance | Test Condition | Test Method | EQUATE KUWAIT/EQUATE PE EGDA-6888 |
|---|---|---|---|
| melting temperature | 内部方法 | 131 °C |