ABS GF10-450 UMG JAPAN
UMG ABS®
--
Filler: Glass fiber reinf、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | UMG JAPAN/GF10-450 |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179 | 3.0 kJ/m² |
| 23°C | ISO179 | 7.0 kJ/m² |
| hardness | Test Condition | Test Method | UMG JAPAN/GF10-450 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO2039-2 | 115 |
| Basic performance | Test Condition | Test Method | UMG JAPAN/GF10-450 |
|---|---|---|---|
| melt mass-flow rate | 13 g/10min |
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/GF10-450 |
|---|---|---|---|
| Charpy impact strength | 7 KJ/m | ||
| Bending stress 3 | 23°C | ISO178 | 116 Mpa |
| Tensile modulus | 23°C | ISO527-2 | 4800 Mpa |
| Flexural modulus | 23°C | ISO178 | 4200 Mpa |
| 4200 Mpa | |||
| Tensile stress | 断裂,23°C | ISO527-2 | 83.0 Mpa |
| flammability | Test Condition | Test Method | UMG JAPAN/GF10-450 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
| physical property | Test Condition | Test Method | UMG JAPAN/GF10-450 |
|---|---|---|---|
| density | 23°C | ISO1183 | 1.11 g/cm³ |
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 13.0 cm3/10min |
| Shrinkage rate | MD：23°C | ISO294-4 | 0.20到0.40 % |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/GF10-450 |
|---|---|---|---|
| 1.8MPa,未退火 | ISO75-2/Af | 98.0 °C | |
| 98 °C | |||
| MD | ISO11359-2 | 5E-05 cm/cm/°C | |
| UL flame retardant rating | UL94 | HB |