Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PAR AXG-1500-30 UNITIKA JAPAN
U-POLYMER
--
Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | UNITIKA JAPAN/AXG-1500-30 |
|---|---|---|---|
| Rockwell hardness | R级 | 121 -- |
| Mechanical properties | Test Condition | Test Method | UNITIKA JAPAN/AXG-1500-30 |
|---|---|---|---|
| compressive strength | MPa | 147 -- | |
| bending strength | MPa | 211 181 | |
| Flexural modulus | MPa | 8200 6300 | |
| tensile strength | MPa | 143 112 | |
| elongation | 断裂 | % | 4.0 6.0 |
| Electrical performance | Test Condition | Test Method | UNITIKA JAPAN/AXG-1500-30 |
|---|---|---|---|
| dielectric strength | kV/mm | -- | |
| arc resistance | sec | 60.0 -- | |
| dielectric constant | 1MHz | 3.60 -- | |
| Dissipation Factor | 1MHz | -- | |
| Volume resistivity | ohms·cm | -- |
| physical property | Test Condition | Test Method | UNITIKA JAPAN/AXG-1500-30 |
|---|---|---|---|
| Shrinkage rate | MD:3.00mm | % | 0.35 -- |
| Water absorption rate | 24hr,3.18mm | % | 0.26 -- |
| Shrinkage rate | TD:3.00mm | % | 0.70 -- |
| Thermal performance | Test Condition | Test Method | UNITIKA JAPAN/AXG-1500-30 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 4.6E-05 -- |
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 179 -- |