PC/ABS NH-1015V K21111 LOTTE KOREA
INFINO® 
Laptop
enhance,transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodLOTTE KOREA/NH-1015V K21111
Charpy Notched Impact Strength23°CISO 179/1eA17 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A14 kJ/m²
hardnessTest ConditionTest MethodLOTTE KOREA/NH-1015V K21111
Rockwell hardnessR级ISO 2039-2118
R级ASTM D785118
Mechanical propertiesTest ConditionTest MethodLOTTE KOREA/NH-1015V K21111
tensile strength 屈服ISO 527-2/5061.0 Mpa
Tensile modulusISO 527-2/502500 Mpa
bending strengthISO 17889.0 Mpa
Flexural modulusISO 1782550 Mpa
bending strengthASTM D79087.0 Mpa
tensile strength 屈服ASTM D63864.0 Mpa
Tensile strain断裂ISO 527-2/5045 %
Flexural modulusASTM D7902400 Mpa
tensile strength 断裂ISO 527-2/5048.0 Mpa
flammabilityTest ConditionTest MethodLOTTE KOREA/NH-1015V K21111
UL flame retardant rating2.0mmUL 945VB
1.5mmUL 94V-0
physical property Test ConditionTest MethodLOTTE KOREA/NH-1015V K21111
Shrinkage rateMD：3.20mmASTM D9550.50-0.70 %
melt mass-flow rate220°C/10.0kgASTM D123830 g/10min
220°C/10.0kgISO 113330 g/10min
Thermal performanceTest ConditionTest MethodLOTTE KOREA/NH-1015V K21111
Heat distortion temperature1.8MPa,Unannealed,4.00mm，HDTISO 75-2/A82.0 °C
1.8MPa,未退火,6.40mm，HDTASTM D64886.0 °C
vicat--ISO 306/B120103 °C
Heat distortion temperature0.45MPa,Unannealed,4.00mm，HDTISO 75-2/B94.0 °C
1.8MPa,Annealed,4.00mm，HDTISO 75-2/A97.0 °C
RTI Imp1.5mmUL 74685.0 °C
vicat--ISO 306/B50100 °C
RTI Str1.5mmUL 74690.0 °C
RTI Elec1.5mmUL 74690.0 °C
Heat distortion temperature0.45MPa,Annealed,4.00mm，HDTISO 75-2/B102 °C