ASA+AES 833A USA Network Polymers
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | USA Network Polymers/ 833A |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C,3.18mm | ASTM D256 | 130 J/m |
| -18°C,3.18mm | ASTM D256 | 150 J/m | |
| 23°C,3.18mm | ASTM D256 | 490 J/m |
| Mechanical properties | Test Condition | Test Method | USA Network Polymers/ 833A |
|---|---|---|---|
| elongation | 屈服 | ASTM D638 | 2.4 % |
| Flexural modulus | ASTM D790 | 1720 MPa | |
| Tensile modulus | ASTM D638 | 2030 MPa | |
| tensile strength | 屈服 | ASTM D638 | 35.2 MPa |
| bending strength | ASTM D790 | 35.9 MPa |
| optical performance | Test Condition | Test Method | USA Network Polymers/ 833A |
|---|---|---|---|
| gloss | 60°,HighGlossSurface,Untextured | ASTM D2457 | 90to100 |
| physical property | Test Condition | Test Method | USA Network Polymers/ 833A |
|---|---|---|---|
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 1.2 g/10min |
| density | ASTM D792 | 1.05 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | USA Network Polymers/ 833A |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTM D696 | 1.7E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 70.5 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTM D696 | 9.2E-05 cm/cm/°C |