PPS 1140L4 SD3002 CELANESE USA
FORTRON®
Fiber grade、During injection molding、Slight flash
Flame retardant、High temperature resistan、enhance、Glass fiber reinforced、Injection grade、Medium melt viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodCELANESE USA/1140L4 SD3002
Charpy Notched Impact Strength23°CISO 179/1eA10 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U34 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA10 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A10 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU53 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A10 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU53 kJ/m²
hardnessTest ConditionTest MethodCELANESE USA/1140L4 SD3002
Rockwell hardnessM级ASTM D785100
M计秤ISO 2039-2100
Supplementary InformationTest ConditionTest MethodCELANESE USA/1140L4 SD3002
Shrinkage rate内部方法3.18 mm
Basic performanceTest ConditionTest MethodCELANESE USA/1140L4 SD3002
Water absorption rateASTM-D5700.02 %
densityISO 11831.65 g/cm³
Mechanical propertiesTest ConditionTest MethodCELANESE USA/1140L4 SD3002
Impact strength of cantilever beam gapISO 180/1A10 kJ/m²
Tensile modulus--ISO 527-2/1A/114700 Mpa
Rockwell hardnessASTM-D785100 R-Scale
Tensile modulus200°CASTM D6383240 Mpa
150°CASTM D6384270 Mpa
tensile strength 断裂ISO 527-2/1A/5195 Mpa
elongation断裂ISO 527-2/1A/51.9 %
tensile strength 断裂,23°CASTM D638200 Mpa
Tensile modulus75°CASTM D63811900 Mpa
ISO 52714700 Mpa
tensile strength ISO 527195 Mpa
bending strengthISO 178285 Mpa
Flexural modulusISO 17814500 Mpa
23°CISO 17814500 Mpa
Tensile modulus-40°CASTM D63814500 Mpa
elongation断裂,23°CASTM D6381.7 %
Electrical performanceTest ConditionTest MethodCELANESE USA/1140L4 SD3002
Dissipation Factor1kHzASTM D1501E-03
dielectric strengthIEC 60243-128 KV/mm
Volume resistivity--ASTM D2571E+16 ohms·cm
dielectric constant1kHzASTM D1503.50
Dissipation Factor1MHzASTM D1501E-03
Volume resistivity--IEC 60093>1.0E+15 ohms·cm
dielectric constant1MHzASTM D1503.50
1MHzIEC 602504.60
Surface ResistivityIEC 60093>1.0E+15 ohms
Dissipation Factor1MHzIEC 602506.2E-03
arc resistanceASTM D495134 sec
Compared to the Leakage Tracking Index (CTI)IEC 60112 V
Biochemical propertiesTest ConditionTest MethodCELANESE USA/1140L4 SD3002
Filling amount40 %
flammabilityTest ConditionTest MethodCELANESE USA/1140L4 SD3002
UL flame retardant rating3.0mmUL 945VA
0.38mmUL 94V-0
1.5mmUL 94V-0
Limiting Oxygen IndexISO 4589-247 %
Filling analysisTest ConditionTest MethodCELANESE USA/1140L4 SD3002
SpecificHeatCapacity of Melt内部方法1500 J/kg/°C
physical property Test ConditionTest MethodCELANESE USA/1140L4 SD3002
Shrinkage rateTDISO 294-40.40-0.60 %
MDASTM D9550.20-0.30 %
MDISO 294-40.20-0.60 %
ISO 294-40.2-0.6 %
densityASTMD7921.65 g/cm³
Water absorption rate饱和,23°CISO 620.020 %
Specific volumeASTM D7920.611 cm³/g
Shrinkage rateTDASTM D9550.50-0.70 %
Thermal performanceTest ConditionTest MethodCELANESE USA/1140L4 SD3002
Heat distortion temperature1.80Mpa，HDTISO 75-A270 °C
1.8MPa,未退火，HDTASTM D648265 °C
melting temperatureISO 11357-3280 °C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A270 °C
Linear coefficient of thermal expansionMDISO 11359-22.6E-05 cm/cm/°C
Heat distortion temperature0.45MPa,退火，HDTASTM D648280 °C
8.0MPa,未退火，HDTISO 75-2/C215 °C
Linear coefficient of thermal expansionTDISO 11359-24.2E-05 cm/cm/°C
UL flame retardant ratingUL 94V-0
Glass Transition TemperatureISO 11357-290.0 °C