MAH-g-copolymer TY 1351 DOW USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | DOW USA/ TY 1351 |
|---|---|---|---|
| Elmendorf tear strength | TD:51µm | ASTM D1922 | 1100 g |
| elongation | TD:断裂,51µm | ASTM D882 | 690 % |
| tensile strength | TD:断裂,51µm | ASTM D882 | 29.2 MPa |
| Dart impact | 51µm | ASTM D1709 | 260 g |
| tensile strength | MD:屈服,51µm | ASTM D882 | 10.5 MPa |
| Secant modulus | 2%正割,MD:51µm | ASTM D882 | 209 MPa |
| 2%正割,TD:51µm | ASTM D882 | 229 MPa | |
| tensile strength | MD:断裂,51µm | ASTM D882 | 36.1 MPa |
| elongation | MD:断裂,51µm | ASTM D882 | 690 % |
| Elmendorf tear strength | MD:51µm | ASTM D1922 | 750 g |
| Thin film puncture strength | 51µm | 内部方法 | 11.6 J/cm³ |
| tensile strength | TD:屈服,51µm | ASTM D882 | 11.3 MPa |
| optical performance | Test Condition | Test Method | DOW USA/ TY 1351 |
|---|---|---|---|
| gloss | 45°,50.8µm | ASTM D2457 | 70 |
| physical property | Test Condition | Test Method | DOW USA/ TY 1351 |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTMD1238 | 2.1 g/10min |
| density | ASTM D792 | 0.923 g/cm³ | |
| Grafting rate of maleic anhydride (MAH) | 内部方法 | Low |
| Thermal performance | Test Condition | Test Method | DOW USA/ TY 1351 |
|---|---|---|---|
| vicat | ASTM D1525 | 98.9 °C | |
| melting temperature | 内部方法 | 123 °C |