PC HFD4412 BK1E808 SABIC INNOVATIVE NANSHA
LEXAN™
Architectural Application、Plastic bag
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD4412 BK1E808 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C6 | ISO 180/1U | 40 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 8.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 830 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 43 kJ/m² |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 21.0 J |
| Suspended wall beam without notch impact strength | 23°C6 | ISO 180/1U | 42 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 48 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD4412 BK1E808 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 110 Mpa |
| Tensile modulus | ASTM D638 | 6400 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 110 Mpa |
| 屈服3 | ASTM D638 | 96.0 Mpa | |
| elongation | 屈服3 | ASTM D638 | 3.0 % |
| bending strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 159 Mpa |
| tensile strength | 断裂3 | ASTM D638 | 96.0 Mpa |
| elongation | 屈服 | ISO 527-2/5 | 2.8 % |
| 断裂 | ISO 527-2/5 | 2.7 % | |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 5850 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD4412 BK1E808 |
|---|---|---|---|
| Burning wire flammability index | 2.0 mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.0 mm | IEC 60695-2-13 | 850 °C |
| UL flame retardant rating | 0.30 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD4412 BK1E808 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.12 % |
| Shrinkage rate | 横向流动 : 3.20 mm | 内部方法 | 0.10 - 0.30 % |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 14.0 cm3/10min |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 15 g/10 min |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.10 - 0.30 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.30 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD4412 BK1E808 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 3.0E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距7，HDT | ISO 75-2/Af | 127 °C |
| Linear coefficient of thermal expansion | 横向 : 23 到 80°C | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| vicat | ISO 306/B120 | 143 °C | |
| Linear coefficient of thermal expansion | 流动 : 23 到 80°C | ISO 11359-2 | 3.0E-5 cm/cm/°C |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 130 °C |
| RTI Imp | UL 746 | 80.0 °C | |
| ball-indentation hardness | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 7.0E-5 cm/cm/°C |
| RTI | UL 746 | 80.0 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 125 °C |
| RTI Elec | UL 746 | 80.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD4412 BK1E808 |
|---|---|---|---|
| screw speed | 40 to 70 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 290 to 310 °C | ||
| drying temperature | 120 °C | ||
| Suggested injection volume | 40 to 60 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 275 to 300 °C | ||
| Temperature at the rear of the barrel | 265 to 290 °C | ||
| Exhaust hole depth | 0.025 to 0.076 mm | ||
| Temperature at the front of the material cylinder | 290 to 310 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 70 to 95 °C | ||
| Spray nozzle temperature | 280 to 305 °C |