Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS NX07344 BK SABIC INNOVATIVE NANSHA
LNP™ THERMOCOMP™
Plastic bag,Gears,Casters
High mobility,High impact resistance,Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/NX07344 BK |
|---|---|---|---|
| 23°C | ISO 180/1A | 6.0 kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.6 kJ/m² |
| 23°C | ISO 180/1U | 21 kJ/m² | |
| ASTM D256 | 60 J/m | ||
| -30°C | ASTM D256 | 44 J/m | |
| ASTM D4812 | 330 J/m | ||
| 23°C | ASTM D4812 | 350 J/m | |
| -30°C | ISO 180/1A | 5.3 kJ/m² | |
| 23°C,TotalEnergy | ASTM D3763 | 11.5 J | |
| -30°C | ISO 180/1U | 21 kJ/m² |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/NX07344 BK |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.0E+4-1.0E+6 ohms·cm | |
| Surface Resistivity | ASTM D257 | 1.0E+3-1.0E+6 ohms | |
| Electromagnetic shielding effectiveness (EMI) | 1.50mm | 内部方法 | 47to53 dB |
| StaticDecay | FTMS101B | 10 msec | |
| Electromagnetic shielding effectiveness (EMI) | 3.00mm | 内部方法 | 60to70 dB |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/NX07344 BK |
|---|---|---|---|
| fracture | ISO 527-2/5 | 62.0 Mpa | |
| ASTM D638 | 1.8 % | ||
| Yield, 50.0mm span | ASTM D790 | 90.0 Mpa | |
| --5 | ISO 178 | 105 Mpa | |
| fracture | ASTM D638 | 60.0 Mpa | |
| Fracture bending strain | ISO 178 | 2.8 % | |
| --1 | ASTM D638 | 6000 Mpa | |
| fracture | ISO 527-2/5 | 1.8 % | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 5300 Mpa |
| Fracture, 50.0mm span | ASTM D790 | 90.0 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/NX07344 BK |
|---|---|---|---|
| UL flame retardant rating | 1.50mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/NX07344 BK |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.38 % |
| 24hr,50%RH | ASTM D570 | 0.080 % | |
| Shrinkage rate | TD | 内部方法 | 0.46 % |
| Balance, 23 ° C, 50% RH | ISO 62 | 0.040 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/NX07344 BK |
|---|---|---|---|
| Flow: 23 to 60 ° C | 23到60℃ | ISO 11359-2 | 2.9E-05 cm/cm/°C |
| Flow: -40 to 40 ° C | ASTME831 | 3.1E-05 cm/cm/°C | |
| Horizontal: -40 to 40 ° C | 横向, -40到40℃ | ASTME831 | 5.8E-05 cm/cm/°C |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 96.0 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 94.0 °C | |
| 1.8MPa, Unanealed, 6.40mm | ASTM D648 | 96.0 °C | |
| Horizontal: 23 to 60 ° C | 横向, 23到60℃ | ISO 11359-2 | 7.4E-05 cm/cm/°C |