PC/PBT HI1002F LG CHEM KOREA
LUPOX®
Electrical field、Electronic field、Electrical/Electronic App
High impact resistance、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG CHEM KOREA/HI1002F |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 690 J/m |
| Electrical performance | Test Condition | Test Method | LG CHEM KOREA/HI1002F |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI)4 | UL 746 | PLC 2 |
| arc resistance | ASTM D495 | PLC 5 |
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/HI1002F |
|---|---|---|---|
| elongation | 断裂,3.20mm | ASTM D638 | >50 % |
| tensile strength | 屈服,3.20mm | ASTM D638 | 49.0 Mpa |
| Flexural modulus | 3.20mm | ASTM D790 | 1960 Mpa |
| bending strength | 屈服,3.20mm | ASTM D790 | 72.6 Mpa |
| flammability | Test Condition | Test Method | LG CHEM KOREA/HI1002F |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 3.0mm | UL 94 | V-0 | |
| 2.3mm | UL 94 | V-0 | |
| 2.0mm | UL 94 | V-0 | |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | LG CHEM KOREA/HI1002F |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 4.0 g/10min |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.90-1.3 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.080 % |
| density | ASTM D792 | 1.33 g/cm³ |
| Thermal performance | Test Condition | Test Method | LG CHEM KOREA/HI1002F |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 90.0 °C |
| melting temperature | ASTM D3418 | 223 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI Str | UL 746 | 120 °C | |
| RTI Elec | UL 746 | 130 °C |