PC/ABS XCY620H SABIC INNOVATIVE US
CYCOLAC™
Home appliance components、Electrical applications
High mobility、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XCY620H |
|---|---|---|---|
| Vicat Softening Temperature | ISO306/B120 | 130 °C | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 106 °C |
| 0.45MPa,未退火,3.20mm | ASTMD648 | 128 °C | |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 126 °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 108 °C | |
| Ball PressureTest | 75°C | IEC60695-10-2 | Pass |
| 100°C10 | IEC60695-10-2 | Pass | |
| Vicat Softening Temperature | ASTMD15259 | 129 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/XCY620H |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.13 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt Volume flow Rate | 265°C/5.0kg | ISO1133 | 25.0 cm3/10min |
| 260°C/5.0kg | ISO1133 | 20.0 cm3/10min | |
| Modeling Shrinkage | TD：3.20mm | 内部方法 | 0.50to0.70 % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.40 % |
| 23°C,24hr | ISO62 | 0.30 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XCY620H |
|---|---|---|---|
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 2300 Mpa |
| ISO178 | 2200 Mpa | ||
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 86.0 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 56.0 Mpa |
| 屈服 | ISO527-2/50 | 54.0 Mpa | |
| Tensile Strain | 断裂 | ISO527-2/50 | 100 % |
| 屈服 | ISO527-2/50 | 4.5 % | |
| Tensile Modulus | ISO527-2/1 | 2200 Mpa | |
| Flexural Stress | ISO178 | 82.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XCY620H |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 40 kJ/m² |
| Instrumented Dart Impact | -30°C,TotalEnergy | ASTMD3763 | 65.0 J |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 45 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 55.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 60 kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 55 kJ/m² |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XCY620H |
|---|---|---|---|
| Dielectric Strength | 3.20mm,在油中 | IEC60243-1 | 17 KV/mm |
| 1.60mm,在油中 | IEC60243-1 | 25 KV/mm | |
| Volume Resistivity | IEC60093 | >1.0E+16 ohms·cm | |
| Dielectric Strength | 0.800mm,在油中 | IEC60243-1 | 39 KV/mm |
| Surface Resistivity | IEC60093 | >1.0E+16 ohms |