PBT+PET SCHULADUR® A1 GF 50 A SCHULMAN USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | A SCHULMAN USA/SCHULADUR® A1 GF 50 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| -30°C | ISO 179/1eA | 10 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
| -30°C | ISO 179/1eU | 60 kJ/m² |
| Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/SCHULADUR® A1 GF 50 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 16000 MPa |
| Tensile modulus | ISO 527-2/1A/1 | 18500 MPa | |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 175 MPa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.5 % |
| bending strength | 23°C | ISO 178 | 245 MPa |
| flammability | Test Condition | Test Method | A SCHULMAN USA/SCHULADUR® A1 GF 50 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | IEC 60695-11-10,-20 | HB |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 825 °C |
| UL flame retardant rating | 3.2mm | IEC 60695-11-10,-20 | HB |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 800 °C |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 725 °C |
| burning rate | ISO 3795 | 25 mm/min | |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 700 °C |
| physical property | Test Condition | Test Method | A SCHULMAN USA/SCHULADUR® A1 GF 50 |
|---|---|---|---|
| density | ISO 1183/A | 1.75 g/cm³ | |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 20.0 cm³/10min |
| Thermal performance | Test Condition | Test Method | A SCHULMAN USA/SCHULADUR® A1 GF 50 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 203 °C |
| vicat | -- | ISO 306/A50 | 218 °C |
| -- | ISO 306/B50 | 201 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 220 °C |