Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ULDPE SL 4102G DOW USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | DOW USA/SL 4102G |
|---|---|---|---|
| Shore hardness | 邵氏D | DIN 53505 | 40 |
| film | Test Condition | Test Method | DOW USA/SL 4102G |
|---|---|---|---|
| Elmendorf tear strength | TD:40µm | ASTM D1922 | 800 g |
| Secant modulus | TD:40µm | ASTM D882 | 95.0 MPa |
| tensile strength | TD:屈服,40µm | ISO 527-3 | 5.40 MPa |
| Dart impact | 40µm | ISO 7765-1/B | >850 g |
| film thickness | 40 µm | ||
| elongation | TD:断裂,40µm | ISO 527-3 | 790 % |
| tensile strength | MD:屈服,40µm | ISO 527-3 | 5.70 MPa |
| TD:断裂,40µm | ISO 527-3 | 30.0 MPa | |
| Elmendorf tear strength | MD:40µm | ASTM D1922 | 660 g |
| Secant modulus | MD:40µm | ASTM D882 | 90.0 MPa |
| elongation | MD:断裂,40µm | ISO 527-3 | 670 % |
| tensile strength | MD:断裂,40µm | ISO 527-3 | 33.0 MPa |
| optical performance | Test Condition | Test Method | DOW USA/SL 4102G |
|---|---|---|---|
| Haze ratio | 40.0µm | ISO 14782 | 7.0 % |
| gloss | 20°,40.0µm | ASTM D2457 | 78 |
| physical property | Test Condition | Test Method | DOW USA/SL 4102G |
|---|---|---|---|
| density | ASTM D792 | 0.905 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 1.0 g/10min |
| Thermal performance | Test Condition | Test Method | DOW USA/SL 4102G |
|---|---|---|---|
| vicat | ASTM D1525 | 84.0 °C | |
| Crystallization peak temperature | DSC | ISO 3146 | 99.0 °C |
| melting temperature | DSC | 122 °C |