Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HF1110-111J SABIC INNOVATIVE JAPAN
LEXAN™
Electronic and electrical、Automotive components
High mobility、High temperature resistan、transparent
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/HF1110-111J |
|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Energy at Peak | ASTM D3763 | 54.0 J |
| Tensile impact strength 4 | ASTM D1822 | 378 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/HF1110-111J |
|---|---|---|---|
| Tensile strength 2 | 屈服 | ASTM D638 | 62.0 Mpa |
| elongation | 断裂 | ASTM D638 | 120 % |
| Tensile strength 2 | 断裂 | ASTM D638 | 65.0 Mpa |
| bending strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 93.0 Mpa |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 2300 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/HF1110-111J |
|---|---|---|---|
| Hot wire ignition (HWI) | UL 746 | PLC 2 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 2 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
| High arc combustion index (HAI) | UL 746 | PLC 1 |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/HF1110-111J |
|---|---|---|---|
| transmissivity | 2540 µm | ASTM D1003 | 88.0 % |
| Haze ratio | 2540 µm | ASTM D1003 | 1.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/HF1110-111J |
|---|---|---|---|
| UL flame retardant rating | 1.1 mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/HF1110-111J |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C | ASTM D570 | 0.35 % |
| 平衡, 100°C | ASTM D570 | 0.58 % | |
| 24 hr | ASTM D570 | 0.10 % | |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 25 g/10 min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/HF1110-111J |
|---|---|---|---|
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 126 °C |
| RTI Imp | UL 746 | 130 °C | |
| RTI | UL 746 | 130 °C | |
| RTI Elec | UL 746 | 130 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/HF1110-111J |
|---|---|---|---|
| Processing (melt) temperature | 270 到 295 °C | ||
| drying temperature | 120 °C | ||
| Exhaust hole depth | 0.025 到 0.076 mm | ||
| Temperature at the front of the material cylinder | 270 到 295 °C | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 260 到 280 °C | ||
| Temperature | 70 到 95 °C | ||
| screw speed | 40 到 70 rpm | ||
| Temperature at the rear of the barrel | 250 到 270 °C | ||
| Back pressure | 0.300 到 0.700 Mpa | ||
| drying time | 3.0 到 4.0 hr | ||
| Suggested injection volume | 40 到 60 % | ||
| Spray nozzle temperature | 265 到 290 °C |