Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA+PC UMG ALLOY® TA-15W UMG JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | UMG JAPAN/UMG ALLOY® TA-15W | |
|---|---|---|---|
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 11.0 cm³/10min |
| density | 23°C | ISO 1183 | 1.12 g/cm³ |
| Tensile modulus | 23°C | ISO 527-2 | 2300 MPa |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8E-05 cm/cm/°C |
| Flexural modulus | 23°C | ISO 178 | 2750 MPa |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 7.0 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 59.0 MPa |
| Shrinkage rate | MD：23°C | ISO 294-4 | 0.50to0.70 % |
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 113 |
| bending strength | 23°C | ISO 178 | 99.0 MPa |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 45 kJ/m² |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 97.0 °C |