PC/ABS LG9000 SABIC INNOVATIVE US
CYCOLAC™
Automotive sector
UV resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 110 °C |
| Linear thermal expansion coefficient | TD：-20to150°C | ASTME831 | 7.2E-05 cm/cm/°C |
| RTIElec | UL746 | 60.0 °C | |
| Linear thermal expansion coefficient | MD：-20to150°C | ASTME831 | 7.2E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 124 °C |
| Thermal Conductivity | ASTMC177 | 0.20 W/m/K | |
| RTIStr | UL746 | 60.0 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 107 °C |
| Vicat Softening Temperature | ASTMD15254 | 129 °C | |
| Evolution Calendar intelligent importer | UL746 | 60.0 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 129 °C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000 |
|---|---|---|---|
| Rockwell Hardness | R级 | ASTMD785 | 118 |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000 |
|---|---|---|---|
| Moisture Absorption | 24hr | ASTMD570 | 0.10 % |
| Density / Specific Gravity | ASTMD792 | 1.13 g/cm³ | |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Moisture Absorption | 平衡,23°C | ASTMD570 | 0.40 % |
| Modeling Shrinkage | TD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt Mass-Flow Rate | 260°C/5.0kg | ASTMD1238 | 17 g/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2310 Mpa |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 84.8 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 75 % |
| Tensile Strength | 屈服 | ASTMD638 | 54.5 Mpa |
| Optical | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000 |
|---|---|---|---|
| Gardner | 60°,无织构 | ASTMD523 | 30 |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000 |
|---|---|---|---|
| Notched Izod Impact Strength | 23°C | ASTMD256 | 530 J/m |
| Instrumented Dart Impact | -30°C,TotalEnergy | ASTMD3763 | 33.9 J |
| Notched Izod Impact Strength | -30°C | ASTMD256 | 320 J/m |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 40.7 J |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000 |
|---|---|---|---|
| Flame Rating | 1.5mm | UL94 | HB |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000 |
|---|---|---|---|
| Arc Resistance | ASTMD495 | PLC6 | |
| Hot-wire Ignition | HWI | UL746 | PLC 2 |
| Comparative Tracking Index | CTI | UL746 | PLC 2 |
| High Amp Arc Ignition | HAI | UL746 | PLC 0 |