Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS Terblend® N NM-12 INEOS Barex
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | INEOS Barex/Terblend® N NM-12 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 17 kJ/m² |
| -30°C | ISO 179 | 9.0 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 17 kJ/m² |
| -30°C | ISO 180/A | 7.0 kJ/m² |
| hardness | Test Condition | Test Method | INEOS Barex/Terblend® N NM-12 |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 102 MPa |
| film | Test Condition | Test Method | INEOS Barex/Terblend® N NM-12 |
|---|---|---|---|
| elongation | 断裂 | 20 % |
| Electrical performance | Test Condition | Test Method | INEOS Barex/Terblend® N NM-12 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 2.90 |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.015 |
| Mechanical properties | Test Condition | Test Method | INEOS Barex/Terblend® N NM-12 |
|---|---|---|---|
| tensile strength | 屈服,23°C | ISO 527-2 | 50.0 MPa |
| Tensile modulus | ISO 527-2 | 2200 MPa | |
| Tensile strain | 屈服,23°C | ISO 527-2 | 3.2 % |
| Flexural modulus | ISO 178 | 2200 MPa | |
| bending strength | ISO 178 | 74.0 MPa |
| physical property | Test Condition | Test Method | INEOS Barex/Terblend® N NM-12 |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.80 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.1 % |
| Melt volume flow rate | 240°C/10.0kg | ISO 1133 | 34.0 cm³/10min |
| density | ISO 1183 | 1.07 g/cm³ |
| Thermal performance | Test Condition | Test Method | INEOS Barex/Terblend® N NM-12 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 9E-05 cm/cm/°C |