HDPE M5363 LYONDELLBASELL HOLAND
Alathon®
chip、cover、container、Barrel、Automotive sector
Compressive crack、High impact resistance、Easy to process、Low odor、Narrow molecular weight d
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LYONDELLBASELL HOLAND/M5363 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -18°C | ASTM D4812 | NoBreak |
| hardness | Test Condition | Test Method | LYONDELLBASELL HOLAND/M5363 |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 70 |
| Mechanical properties | Test Condition | Test Method | LYONDELLBASELL HOLAND/M5363 |
|---|---|---|---|
| Flexural modulus | 1%正割 | ASTM D790 | 1290 Mpa |
| tensile strength | Break | ASTM D638 | 24.1 Mpa |
| Tensile modulus | -- | ASTM D638 | 1030 Mpa |
| Tensile strain | Yield | ASTM D638 | 8.5 % |
| tensile strength | 屈服 | ASTM D638 | 28.1 Mpa |
| Tensile strain | Break | ASTM D638 | 1500 % |
| Tensile modulus | 1%正割 | ASTM D638 | 809 Mpa |
| Flexural modulus | -- | ASTM D790 | 1440 Mpa |
| 2%正割 | ASTM D790 | 1070 Mpa |
| physical property | Test Condition | Test Method | LYONDELLBASELL HOLAND/M5363 |
|---|---|---|---|
| Apparent density | ASTM D1895 | 0.53to0.59 g/cm³ | |
| spiral flow length | 内部方法 | 22.6 CM | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 6.5 g/10min |
| Thermal performance | Test Condition | Test Method | LYONDELLBASELL HOLAND/M5363 |
|---|---|---|---|
| vicat | ASTM D1525 | 126 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 74.0 °C |
| brittle temperature | ASTM D746 | <-76.0 °C | |
| melting temperature | ASTM D3418 | 130 °C | |
| Crystallization peak temperature | DSC)12 | ASTM D3418 | 117 °C |