Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS TM-25M UMG JAPAN
UMG ABS®
--
heat-resisting
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodUMG JAPAN/TM-25M
Rockwell hardnessR计秤,23°CISO 2039-2113
Basic performanceTest ConditionTest MethodUMG JAPAN/TM-25M
melt mass-flow rate4 g/10min
Mechanical propertiesTest ConditionTest MethodUMG JAPAN/TM-25M
Impact strength of cantilever beam gapASTM D256/ISO 17917 kg·cm/cm(J/M)ft·lb/in
bending strengthASTM D790/ISO 17866 kg/cm²(MPa)[Lb/in²]
Flexural modulusASTM D790/ISO 1782500 kg/cm²(MPa)[Lb/in²]
bending strength23°CISO 17866.0 Mpa
Flexural modulus2500 Mpa
23°CISO 1782500 Mpa
Tensile modulus23°CISO 527-22400 Mpa
ASTM D638/ISO 5272400 kg/cm²(MPa)[Lb/in²]
Rockwell hardnessASTM D785113
Charpy Notched Impact Strength17 KJ/m
tensile strength ASTM D638/ISO 52745 kg/cm²(MPa)[Lb/in²]
23°CISO 527-245.0 Mpa
Physical propertiesTest ConditionTest MethodUMG JAPAN/TM-25M
Shrinkage rateASTM D9550.4-0.6 %
densityASTM D792/ISO 11831.06
melt mass-flow rateASTM D1238/ISO 11334 g/10min
flammabilityTest ConditionTest MethodUMG JAPAN/TM-25M
UL flame retardant rating1.5mmUL 94HB
physical property Test ConditionTest MethodUMG JAPAN/TM-25M
Shrinkage rateMD:23°CISO 294-40.40-0.60 %
Melt volume flow rate220°C/10.0kgISO 11334.00 cm3/10min
Thermal performanceTest ConditionTest MethodUMG JAPAN/TM-25M
Heat distortion temperatureHDT98 °C
1.8MPa,未退火,HDTISO 75-2/Af98.0 °C
Combustibility (rate)UL 941.5 HB
Heat distortion temperatureHDTASTM D648/ISO 7598 ℃(℉)
Linear coefficient of thermal expansionMDISO 11359-29E-05 cm/cm/°C
ASTM D696/ISO 113599 mm/mm.℃
UL flame retardant ratingUL 94HB