LDPE AT 525 CELANESE USA
--
sealant、adhesive、film
High mobility、Bondable
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | CELANESE USA/AT 525 |
|---|---|---|---|
| tensile breaking strength | MD，35µm | ASTM D-882A | 29 MPa |
| Falling hammer impact | 35µm | ASTM D-1709 | 74 g |
| 1% secant modulus | MD，35µm | ASTM D-882 | 230 MPa |
| tensile yield strength | TD | 13 | |
| Tensile fracture strength of film | ASTMD882 | 22 Mpa | |
| 1% secant modulus | TD | 270 | |
| elongation at break | TD | 610 | |
| MD，35µm | ASTM D-882 | 400 % | |
| Tensile strength of film | ASTMD882 | 13 Mpa | |
| ASTM D-1894 | 0.45 | ||
| tensile breaking strength | TD | 22 | |
| The elongation at break of the membrane | ASTMD882 | 610 % |
| optical performance | Test Condition | Test Method | CELANESE USA/AT 525 |
|---|---|---|---|
| Haze ratio | ASTMD1003 | 9.0 % |
| physical property | Test Condition | Test Method | CELANESE USA/AT 525 |
|---|---|---|---|
| film thickness | DSC | ||
| melt mass-flow rate | 190℃/2.16kg | ASTM D-1238 | 0.80 g/10min |
| 190℃/2.16Kg | ASTMD1238 | 0.80 g/10min |
| Thermal performance | Test Condition | Test Method | CELANESE USA/AT 525 |
|---|---|---|---|
| vicat | ASTM1525 | 99.8 °C |