PC/ABS 7410 SABIC INNOVATIVE SINGAPHORE
CYCOLOY™
Automotive interior parts、Electrical applications、Thin walled components
Flame retardant、High impact resistance、Filler: Talc filler
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE SINGAPHORE/7410
Melt Volume-Flow Rate (MVR)
260°C/2.16kg
ISO1133
cm3/10min
1
Melt mass flow rate
260°C/2.16kg
ASTMD1238
g/10min
1
Shrinkage rate
MD:3.20mm
内部方法
%
0
Shrinkage rate
TD:3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE SINGAPHORE/7410
--
ASTMD638
Mpa
3
--
ISO527-2/1
Mpa
3
--
ISO178
Mpa
3
--
ISO178
Mpa
9
23°C
ISO180/1A
kJ/m²
3
23°C
ASTMD256
J/m
3
-30°C
ISO180/1A
kJ/m²
7
-30°C
ASTMD256
J/m
7
50.0mm span
ASTMD790
Mpa
3
Fracture
ASTMD638
%
7
crack
ISO527-2/5
%
7
Fracture
ASTMD638
Mpa
4
crack
ISO527-2/5
Mpa
3
The impact strength of a simply supported beam with a notch of
23°C
ISO179/1eA
kJ/m²
1
Surrender
ASTMD638
%
3
yield
ISO527-2/5
%
3
yield
ISO527-2/5
Mpa
5
Surrender
ASTMD638
Mpa
5
Yield, 50.0mm span
ASTMD790
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE SINGAPHORE/7410
--
ISO 1183
°C
1
--
ISO306/B120
°C
1
1.8MPa, unannealed, 3.20mm
ASTMD648
°C
8
1.8MPa, unannealed, 6.40mm
ASTMD648
°C
8
1.8MPa, unannealed, 64.0mm span
ISO75-2/Af
°C
8
Linear coefficient of thermal expansion
MD:-40到40°C
ASTME831,ISO11359-2
cm/cm/°C
6
Linear coefficient of thermal expansion
TD:-40到40°C
ASTME831,ISO11359-2
cm/cm/°C
6