Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS HG-0760AT Samsung Cheil South Korea
STAREX®
Electrical enclosure、Automotive Applications
High mobility、Antistatic、High impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/Samsung Cheil South Korea/HG-0760AT
density
ASTMD792
g/cm³
1
density
ISO1183
g/cm³
1
Melt mass flow rate
200°C/5.0kg
ASTMD1238
g/10min
3
Melt mass flow rate
200°C/5.0kg
ISO1133
g/10min
3
Shrinkage rate
MD：3.20mm
ASTMD955
%
0
Shrinkage rate
TD：3.20mm
ASTMD955
%
0
Shrinkage rate
TD:3.20mm
ISO2577
%
0
Shrinkage rate
MD:3.20mm
ISO2577
%
0
Mechanical performance
Test Condition
Test Method
Unit
ABS/Samsung Cheil South Korea/HG-0760AT
CharpyNotchedImpactStrength
23°C
ISO179/1eA
kJ/m²
1
Tensile modulus
ASTMD638
Mpa
2
Tensile modulus
ISO527-2/50
Mpa
2
tensile strength
屈服
ASTMD638
Mpa
3
tensile strength
屈服
ISO527-2/50
Mpa
4
tensile strength
断裂
ASTMD638
Mpa
3
tensile strength
断裂
ISO527-2/50
Mpa
3
elongation
断裂
ASTMD638
%
3
elongation
断裂
ISO527-2/50
%
2
Bending modulus
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
Bending strength
ASTMD790
Mpa
6
bending strength
ISO178
Mpa
6
Impact strength of cantilever beam gap
23°C,3.18mm
ASTMD256
J/m
2
Impact strength of cantilever beam gap
23°C,6.35mm
ASTMD256
J/m
2
Suspended wall beam gap impact strength
23°C
ISO180/1A
kJ/m²
1
Thermal performance
Test Condition
Test Method
Unit
ABS/Samsung Cheil South Korea/HG-0760AT
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
8
Hot deformation temperature
1.8MPa,Unannealed,4.00mm
ISO75-2/A
°C
8
vicat softening point
ISO306/B50
°C
9
Contact Us
Get App