Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI JL-4030 BK SABIC INNOVATIVE US
ULTEM™
Electronic and electrical
Hydrolysis resistance、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/JL-4030 BK |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 55 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 6.1 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/JL-4030 BK |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 9.9 % |
| bending strength | ISO 178 | 79.0 Mpa | |
| coefficient of friction | Static | ASTM D3702Modified | 0.13 |
| bending strength | ASTM D790 | 75.8 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 12 % |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| Wear factor | Washer | ASTM D3702Modified | 24.5 10^-10in^5-min/ft-lb-hr |
| tensile strength | 断裂 | ASTM D638 | 55.2 Mpa |
| 断裂 | ISO 527-2 | 55.0 Mpa | |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.23 |
| Flexural modulus | ASTM D790 | 2070 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/JL-4030 BK |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.76 % |
| MD：24小时 | ASTM D955 | 0.70-0.90 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.10 % |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.70-0.90 % |
| TD:24小时 | ISO 294-4 | 0.83 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/JL-4030 BK |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 179 °C |
| 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 178 °C | |
| 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 169 °C | |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 170 °C |