LLDPE TOTAL Polyethylene Lotrène® Q2018 C TOTAL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | TOTAL/TOTAL Polyethylene Lotrène® Q2018 C |
|---|---|---|---|
| tensile strength | TD:断裂,20µm,挤塑薄膜 | ISO 527-3 | 23.0 MPa |
| Elmendorf tear strength | MD:20µm,铸造薄膜 | ISO 6383-2 | 12 N |
| tensile strength | TD:屈服,20µm,挤塑薄膜 | ISO 527-3 | 9.60 MPa |
| Elmendorf tear strength | TD:20µm,铸造薄膜 | ISO 6383-2 | 190 N |
| Tensile modulus | 1%正割,TD:20µm,铸造薄膜 | ISO 178 | 170 MPa |
| Dart impact | 20µm,CastFilm | ISO 7765-1 | 35 g |
| elongation | MD:断裂,20µm,挤塑薄膜 | ISO 527-3 | 330 % |
| Tensile modulus | 1%正割,MD:20µm,铸造薄膜 | ISO 178 | 165 MPa |
| film thickness | 20 µm | ||
| tensile strength | MD:断裂,20µm,挤塑薄膜 | ISO 527-3 | 37.0 MPa |
| MD:屈服,20µm,挤塑薄膜 | ISO 527-3 | 9.70 MPa | |
| elongation | TD:断裂,20µm,挤塑薄膜 | ISO 527-3 | 670 % |
| optical performance | Test Condition | Test Method | TOTAL/TOTAL Polyethylene Lotrène® Q2018 C |
|---|---|---|---|
| gloss | 45°,20.0µm,铸造薄膜 | ASTM D2457 | 92 |
| Haze ratio | 20.0µm,铸造薄膜 | ISO 14782 | 1.8 % |
| physical property | Test Condition | Test Method | TOTAL/TOTAL Polyethylene Lotrène® Q2018 C |
|---|---|---|---|
| density | ASTM D792 | 0.918 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 2.0 g/10min |
| Thermal performance | Test Condition | Test Method | TOTAL/TOTAL Polyethylene Lotrène® Q2018 C |
|---|---|---|---|
| melting temperature | 内部方法 | 121 °C | |
| vicat | ASTM D15253 | 100 °C |