Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

ABS PA-756K ZHENJIANG CHIMEI
POLYLAC®
small home appliances、Home appliance components
High mobility、Qui-gon 、High gloss
MSDS
SGS
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | ZHENJIANG CHIMEI/PA-756K |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179 | 17 kJ/m² |
Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 170 J/m |
23°C,6.40mm | ASTM D256 | 160 J/m | |
Charpy Notched Impact Strength | -30°C | ISO 179 | 9.0 kJ/m² |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 kJ/m² |
23°C | ISO 180/1A | 16 kJ/m² |
hardness | Test Condition | Test Method | ZHENJIANG CHIMEI/PA-756K |
---|---|---|---|
Rockwell hardness | R级 | ASTM D785 | 115 |
Mechanical properties | Test Condition | Test Method | ZHENJIANG CHIMEI/PA-756K |
---|---|---|---|
tensile strength | 屈服4 | ASTM D638 | 46.9 Mpa |
屈服 | ISO 527-2/50 | 45.0 Mpa | |
elongation | 断裂4 | ASTM D638 | 20 % |
bending strength | --5 | ASTM D790 | 74.3 Mpa |
--6 | ISO 178 | 72.0 Mpa | |
elongation | 断裂 | ISO 527-2/50 | 30 % |
Flexural modulus | --6 | ISO 178 | 2100 Mpa |
--5 | ASTM D790 | 2550 Mpa | |
tensile strength | 断裂 | ISO 527-2/50 | 32.0 Mpa |
flammability | Test Condition | Test Method | ZHENJIANG CHIMEI/PA-756K |
---|---|---|---|
UL flame retardant rating | 1.5mm | UL 94 | HB |
physical property | Test Condition | Test Method | ZHENJIANG CHIMEI/PA-756K |
---|---|---|---|
density | 23°C | ISO 1183 | 1.05 g/cm³ |
melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 4.4 g/10min |
Shrinkage rate | ISO 294-4 | 0.40-0.70 % | |
density | --3 | ASTM D792 | 1.05 g/cm³ |
Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 40.0 cm3/10min |
Thermal performance | Test Condition | Test Method | ZHENJIANG CHIMEI/PA-756K |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTMD648 | 83.0 °C |
vicat | -- | ASTM D15257 | 105 °C |
Heat distortion temperature | 1.8MPa,退火,HDT | ASTM D648 | 95.0 °C |
vicat | -- | ISO 306/A50 | 104 °C |
Heat distortion temperature | 1.8MPa,退火,HDT | ISO 75-2/A | 98.0 °C |
vicat | -- | ISO 306/B50 | 96.0 °C |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.9E-05 cm/cm/°C |