Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP 7130 BK010 CELANESE USA
ZENITE®
Automotive Applications、Home appliance components、Medical/nursing supplies
enhance、Glass fiber reinforced、High impact resistance、heat-resisting、Filler: Glass fiber reinf、30%、Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/7130 BK010 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 30 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 30 kJ/m² |
| -30°C | ISO 179/1eU | 22 kJ/m² |
| Electrical performance | Test Condition | Test Method | CELANESE USA/7130 BK010 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| dielectric strength | IEC 60243-1 | 45 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 4.10 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.014 |
| relative permittivity | 1MHz | IEC 60250 | 3.70 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.030 |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/7130 BK010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 17000 Mpa | |
| bending strength | 23°C | ISO 178 | 210 Mpa |
| Flexural modulus | 23°C | ISO 178 | 13000 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 150 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.5 % |
| other | Test Condition | Test Method | CELANESE USA/7130 BK010 |
|---|---|---|---|
| characteristic | 耐高温 高刚性 | ||
| purpose | 车辆配件 |
| flammability | Test Condition | Test Method | CELANESE USA/7130 BK010 |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 45 % | |
| UL flame retardant rating | 0.40mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | CELANESE USA/7130 BK010 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.60 % |
| MD | ISO 294-4 | 0.010 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/7130 BK010 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 352 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 310 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 3E-06 cm/cm/°C |
| TD | ISO 11359-2 | 6.2E-05 cm/cm/°C | |
| Glass Transition Temperature | ISO 11357-2 | 120 °C |