PC 915AU BK1E366T SABIC INNOVATIVE US
LEXAN™ 
Electrical applications、Lighting applications
Thermal stability、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/915AU BK1E366T
23°CISO 180/1A65 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Dart impact23°C,TotalEnergyASTM D376360.0 J
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
-30°CASTM D256110 J/m
ISO 179/1eA12 kJ/m²
23°CISO 179/1eA65 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA65 kJ/m²
23°CASTM D256650 J/m
Charpy Notched Impact Strength-30°CISO 179/1eA12 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
23°CISO 179/2C11 kJ/m²
-30°CISO 180/1A11 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/915AU BK1E366T
Tensile modulus--2ASTM D6382400 Mpa
bending strength屈服,50.0mm跨距4ASTM D79095.0 Mpa
tensile strength 屈服3ASTM D63866.0 Mpa
elongation断裂3ASTM D638100 %
yieldASTM D63866.0 Mpa
ISO 527-2/5066.0 Mpa
Yield, 50.0mm spanASTM D79095.0 Mpa
elongation断裂ISO 527-2/50100 %
Flexural modulus50.0mm跨距4ASTM D7902400 Mpa
fractureISO 527-2/5066.0 Mpa
bending strength--5,6ISO 17898.0 Mpa
tensile strength 断裂ISO 527-2/5066.0 Mpa
屈服ISO 527-2/5066.0 Mpa
fractureISO 527-2/50100 %
yieldISO 527-2/506.0 %
elongation屈服3ASTM D6386.0 %
--8ISO 1782400 Mpa
tensile strength 断裂3ASTM D63866.0 Mpa
yieldASTM D6386.0 %
--2ASTM D6382400 Mpa
Flexural modulus--5ISO 1782400 Mpa
fractureASTM D63866.0 Mpa
ASTM D638100 %
elongation屈服ISO 527-2/506.0 %
--9ISO 17898.0 Mpa
50.0mm spanASTM D7902400 Mpa
Tensile modulus--ISO 527-2/12400 Mpa
optical performance Test ConditionTest MethodSABIC INNOVATIVE US/915AU BK1E366T
refractive indexISO 4891.586
transmissivity2540µmASTM D100388.0 %
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/915AU BK1E366T
UL flame retardant rating3.00mmUL 94V-0
3.0mmUL 94V-0
1.50mmUL 94V-2
1.5mmUL 94V-2
physical property Test ConditionTest MethodSABIC INNOVATIVE US/915AU BK1E366T
Shrinkage rateMD：3.20mm内部方法0.50-0.70 %
Melt volume flow rate300°C/1.2kgISO 113321.0 cm3/10min
Shrinkage rateMD：--1内部方法0.50-0.70 %
Water absorption rate平衡,23°C,50%RHISO 620.15 %
饱和,23°CISO 620.35 %
melt mass-flow rate300°C/1.2kgASTM D123823 g/10min
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/915AU BK1E366T
vicat--ISO 306/B120141 °C
0.45MPa, Unanealed, 100mm spanISO 75-2/Be134 °C
Linear coefficient of thermal expansionTD:-40到40°CASTME8317E-05 cm/cm/°C
Flow: -40 to 40 ° CASTME8317E-05 cm/cm/°C
1.8MPa, Unanealed, 100mm spanISO 75-2/Ae123 °C
Horizontal: -40 to 40 ° C横向, -40到40℃ASTME8317E-05 cm/cm/°C
vicat--ASTMD152510140 °C
Heat distortion temperature1.8MPa,未退火,100mm跨距9，HDTISO 75-2/Ae123 °C
1.8MPa, Unanealed, 3.20mmASTM D648125 °C
Heat distortion temperature1.8MPa,未退火,3.20mm，HDTASTM D648125 °C
Linear coefficient of thermal expansionMD:-40到40°CASTME8317E-05 cm/cm/°C