ABS PRL ABS-GP-HH Polymer Resources Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Polymer Resources Ltd./PRL ABS-GP-HH |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 11 kJ/m² |
| Impact strength of cantilever beam gap | -40°C,3.18mm | ASTM D256 | 53 J/m |
| 23°C | ISO 180/1A | 13 kJ/m² | |
| -40°C | ISO 180/1A | 6.3 kJ/m² | |
| Dart impact | 3.18mm | ASTM D3029 | 22.6 J |
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 190 J/m |
| hardness | Test Condition | Test Method | Polymer Resources Ltd./PRL ABS-GP-HH |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 112 |
| Mechanical properties | Test Condition | Test Method | Polymer Resources Ltd./PRL ABS-GP-HH |
|---|---|---|---|
| elongation | 断裂,3.18mm | ASTM D638 | 25 % |
| Flexural modulus | 3.18mm | ASTM D790 | 2480 MPa |
| Tensile modulus | 3.18mm | ASTM D638 | 2210 MPa |
| tensile strength | 屈服,3.18mm | ASTM D638 | 44.8 MPa |
| 断裂,3.18mm | ASTM D638 | 42.1 MPa | |
| elongation | 屈服,3.18mm | ASTM D638 | 4.5 % |
| bending strength | 3.18mm | ASTM D790 | 79.3 MPa |
| physical property | Test Condition | Test Method | Polymer Resources Ltd./PRL ABS-GP-HH |
|---|---|---|---|
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 1.0to5.0 g/10min |
| density | ASTM D792 | 1.05 g/cm³ | |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 0.50to0.70 % |
| Thermal performance | Test Condition | Test Method | Polymer Resources Ltd./PRL ABS-GP-HH |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.18mm，HDT | ASTM D648 | 102 °C |
| 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 90.6 °C | |
| vicat | ASTM D15252 | 116 °C |