Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
Plastomer, Ethylene-based Premi-Glas® 1200H-20 USA Premix
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | USA Premix/Premi-Glas® 1200H-20 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 模压成型 | ASTM D4812 | 800 J/m |
| Impact strength of cantilever beam gap | 模压成型 | ASTM D256 | 530 J/m |
| Mechanical properties | Test Condition | Test Method | USA Premix/Premi-Glas® 1200H-20 |
|---|---|---|---|
| Flexural modulus | 模压成型 | ASTM D790 | 10300 MPa |
| compressive strength | ASTM D695 | 165 MPa | |
| Tensile modulus | 模压成型 | ASTM D638 | 11700 MPa |
| tensile strength | 模压成型 | ASTM D638 | 48.3 MPa |
| bending strength | 模压成型 | ASTM D790 | 124 MPa |
| Poisson's ratio | 0.30 |
| Electrical performance | Test Condition | Test Method | USA Premix/Premi-Glas® 1200H-20 |
|---|---|---|---|
| dielectric strength | ASTM D149 | 15 kV/mm | |
| arc resistance | ASTM D495 | 180 sec |
| flammability | Test Condition | Test Method | USA Premix/Premi-Glas® 1200H-20 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | USA Premix/Premi-Glas® 1200H-20 |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.010 % | |
| Outdoor applicability | UL 746C | f1 |
| Thermal performance | Test Condition | Test Method | USA Premix/Premi-Glas® 1200H-20 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD3 | 2.5E-05 cm/cm/°C | |
| thermal conductivity | 0.30 W/m/K | ||
| RTI Imp | UL 746 | 130 °C | |
| Linear coefficient of thermal expansion | TD4 | 3.5E-05 cm/cm/°C | |
| RTI Str | UL 746 | 130 °C | |
| RTI Elec | UL 746 | 130 °C |