Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM GH-25 PTM NANTONG
--
--
Filler: Glass fiber reinf、25% filler by weight、25% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | PTM NANTONG/GH-25 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| Supplementary Information | Test Condition | Test Method | PTM NANTONG/GH-25 |
|---|---|---|---|
| ColorNumber | CF3500/CD3501 |
| hardness | Test Condition | Test Method | PTM NANTONG/GH-25 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 90 |
| Mechanical properties | Test Condition | Test Method | PTM NANTONG/GH-25 |
|---|---|---|---|
| Wear factor | 0.060MPa,0.15m/sec7 | JISK7218 | 10000 10^-8mm³/N·m |
| Tensile modulus | ISO 527-2 | 8500 Mpa | |
| coefficient of friction | 与钢-动态3 | JISK7218 | 0.60 |
| bending strength | ISO 178 | 200 Mpa | |
| Wear factor | 0.49MPa,0.30m/sec5 | JISK7218 | 400 10^-8mm³/N·m |
| Tensile strain | 断裂 | ISO 527-2 | 2.8 % |
| Flexural modulus | ISO 178 | 7900 Mpa | |
| coefficient of friction | Dynamic2 | JISK7218 | 0.37 |
| Wear factor | 0.49MPa,0.30m/sec6 | JISK7218 | 8000 10^-8mm³/N·m |
| tensile strength | ISO 527-2 | 136 Mpa | |
| Wear factor | 0.060MPa,0.15m/sec4 | JISK7218 | 300 10^-8mm³/N·m |
| Electrical performance | Test Condition | Test Method | PTM NANTONG/GH-25 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 5E+13 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 24 KV/mm |
| Surface Resistivity | IEC 60093 | 9E+15 ohms |
| flammability | Test Condition | Test Method | PTM NANTONG/GH-25 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | PTM NANTONG/GH-25 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 1.80 cm3/10min |
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.60 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.70 % |
| density | ISO 1183 | 1.59 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 2.5 g/10min |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.90 % |
| Thermal performance | Test Condition | Test Method | PTM NANTONG/GH-25 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 9E-05 cm/cm/°C |
| MD：23到55°C | 内部方法 | 3E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 162 °C |