PPO(PPE) PRL PPX/NY-GP2 Polymer Resources Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Polymer Resources Ltd./PRL PPX/NY-GP2 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C,3.18mm | ASTM D256 | 110 J/m |
| Dart impact | 3.18mm | ASTM D3029 | 28.2 J |
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 190 J/m |
| hardness | Test Condition | Test Method | Polymer Resources Ltd./PRL PPX/NY-GP2 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 116 |
| Mechanical properties | Test Condition | Test Method | Polymer Resources Ltd./PRL PPX/NY-GP2 |
|---|---|---|---|
| elongation | 断裂,3.18mm | ASTM D638 | 50 % |
| Flexural modulus | 3.17mm | ASTM D790 | 2210 MPa |
| tensile strength | 屈服,3.17mm | ASTM D638 | 57.9 MPa |
| Break,3.18mm | ASTM D638 | 55.2 MPa | |
| bending strength | 3.18mm | ASTM D790 | 93.1 MPa |
| physical property | Test Condition | Test Method | Polymer Resources Ltd./PRL PPX/NY-GP2 |
|---|---|---|---|
| Shrinkage rate | TD：3.18mm | ASTM D955 | 0.90to1.2 % |
| melt mass-flow rate | 300°C/3.8kg | ASTM D1238 | 10to30 g/10min |
| density | ASTM D792 | 1.10 g/cm³ | |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 1.0to1.3 % |
| Thermal performance | Test Condition | Test Method | Polymer Resources Ltd./PRL PPX/NY-GP2 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.18mm，HDT | ASTM D648 | 154 °C |
| 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 129 °C | |
| vicat | ASTM D15252 | 199 °C |