Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS A512 XO2 TORAY JAPAN
Torelina®
engineering application 、Phone、Automotive components、battery
Thermal stability、Filler: Carbon fiber rein、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPS/TORAY JAPAN/A512 XO2
PVLimit
vs.S45C
SuzukiMethod
MPa·m/s
2
PVLimit
vs.SUS
SuzukiMethod
MPa·m/s
2
Shrinkage rate
TD:3.00mm2
内部方法
%
0
Shrinkage rate
MD:3.00mm3
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPS/TORAY JAPAN/A512 XO2
AmountofWear
vs.S45C
SuzukiMethod
mg/hr
0
AmountofWear
vs.SUS
SuzukiMethod
mg/hr
0
tensile strength
23°C
ISO527-2
Mpa
1
elongation
断裂,23°C
ISO527-2
%
1
Bending modulus
23°C
ISO178
Mpa
9
bending strength
23°C
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PPS/TORAY JAPAN/A512 XO2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Melting temperature
DSC
°C
2
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
2
Electrical performance
Test Condition
Test Method
Unit
PPS/TORAY JAPAN/A512 XO2
Volume resistivity
IEC60093
ohms·cm
1