PC/ABS MB8300 NAT MITSUBISHI ENGINEERING JAPAN
IUPILON™
Electronic and Electrical Applications
High mobility,heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB8300 NAT |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB8300 NAT |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2800 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 69 % | |
| bending strength | ISO 178 | 98.0 Mpa | |
| Flexural modulus | ISO 178 | 2700 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 4.0 % |
| tensile strength | 屈服 | ISO 527-2 | 59.0 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB8300 NAT |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB8300 NAT |
|---|---|---|---|
| UL flame retardant rating | 2.0mm | UL 94 | 5VB |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB8300 NAT |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.30-0.50 % | |
| Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 17.0 cm3/10min |
| Shrinkage rate | MD:3.20mm | 0.30-0.50 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.20 % |
| melt mass-flow rate | 260°C/2.16kg | ISO 1133 | 18 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB8300 NAT |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 95.0 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 87.0 °C |