POM F10-01 MITSUBISHI ENGINEERING JAPAN
Iupital™
Automotive sector,Electrical field,Electronic field,Pipeline components
copolymer,Fatigue resistance,Chemical resistance,Anti creep,Good liquidity,Good forming performance,Thermal stability,wear resistant,high viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/F10-01 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 1.E+16 Ω | |
| dielectric constant | ASTM D150/IEC 60250 | 3.9 | |
| arc resistance | ASTM D495/IEC 60112 | 600 | |
| Volume resistivity | ASTM D257/IEC 60093 | 1.E+12 Ω.cm |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/F10-01 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 89 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2500 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ASTM D638/ISO 527 | 2800 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | 33 % |
| other | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/F10-01 |
|---|---|---|---|
| characteristic | 挤出级 |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/F10-01 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 2.2 % | |
| density | ASTM D792/ISO 1183 | 1.41 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.22 % |
| processability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/F10-01 |
|---|---|---|---|
| process temperature | 180-210 °C | ||
| Dry conditions | 热风干燥 80℃---约3-4小时 | ||
| screw speed | 80-120 rpm | ||
| Temperature | 60-80 °C |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/F10-01 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1.1E-04 mm/mm.℃ |