Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 1500G15 SAMYANG KOREA
TRIBIT®
Laptop case、Automotive sector、Phone case、Engine parts
Medium viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | SAMYANG KOREA/1500G15 |
|---|---|---|---|
| UL flame retardant rating | 1/6＂英寸 | UL -94 | HB |
| Conductivity | 10 | ASTM D-150 | 3.2 |
| hardness | Test Condition | Test Method | SAMYANG KOREA/1500G15 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 119 |
| Mechanical properties | Test Condition | Test Method | SAMYANG KOREA/1500G15 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 7 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 1500 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D-785 | 119 R scale | |
| Flexural modulus | ASTM D790/ISO 178 | 50000 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | 7 % | |
| Rockwell hardness | ASTM D785 | 119 | |
| Flexural modulus | ASTM D790 | 4900 Mpa | |
| tensile strength | ASTM D638/ISO 527 | 1100 kg/cm²(MPa)[Lb/in²] | |
| elongation | 断裂 | ASTM D-638 | 7 % |
| 断裂 | ASTM D638 | 7.0 % | |
| bending strength | 屈服 | ASTM D790 | 147 Mpa |
| Impact strength of cantilever beam gap | 1/8＂英寸 | ASTM D-256 | 1/8＂英寸 kg.cm/cm |
| tensile strength | ASTM D-638 | 1100 kg/cm | |
| Flexural modulus | ASTM D-790 | 50000 kg/cm | |
| tensile strength | 屈服 | ASTM D638 | 108 Mpa |
| bending strength | ASTM D-790 | 1500 kg/cm |
| Electrical performance | Test Condition | Test Method | SAMYANG KOREA/1500G15 |
|---|---|---|---|
| dielectric strength | ASTM D-257 | 21 KV/mm | |
| Volume resistivity | ASTM D257 | 1E+16 ohms·cm | |
| Dissipation Factor | ASTM D150 | 0.020 | |
| Volume resistivity | 1016 | ASTM D-257 | 10 Ω.cm |
| Dissipation Factor | 10 | ASTM D-150 | 0.02 |
| dielectric strength | ASTM D149 | 21 KV/mm | |
| arc resistance | ASTM D-495 | 150 sec | |
| Volume resistivity | ASTM D257/IEC 60093 | 1 Ω.cm | |
| dielectric constant | ASTM D150 | 3.20 | |
| arc resistance | ASTM D495 | 150 sec |
| other | Test Condition | Test Method | SAMYANG KOREA/1500G15 |
|---|---|---|---|
| characteristic | 玻纤增强 |
| Physical properties | Test Condition | Test Method | SAMYANG KOREA/1500G15 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.5 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 60 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.08 % |
| flammability | Test Condition | Test Method | SAMYANG KOREA/1500G15 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | SAMYANG KOREA/1500G15 |
|---|---|---|---|
| Water absorption rate | ASTM D-570 | 0.08 % | |
| Shrinkage rate | MD | ASTM D955 | 0.20-1.2 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.080 % |
| melt mass-flow rate | 250°C/5.0kg | ASTM D1238 | 85 g/10min |
| Thermal performance | Test Condition | Test Method | SAMYANG KOREA/1500G15 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 210 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 225 °C | |
| 18.6kg/cm，HDT | ASTM D-648 | 210 °C | |
| HDT | ASTM D648/ISO 75 | 210 ℃（℉） | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 3E-05 cm/cm/°C |
| melting temperature | 224 °C | ||
| Heat distortion temperature | 4.6kg/cm，HDT | ASTM D-648 | 225 °C |
| Linear coefficient of thermal expansion | ASTM D-696 | 3 mm/mm/℃ | |
| ASTM D696/ISO 11359 | 3 mm/mm.℃ |