PC AC3854 FCFC TAIWAN
TAIRILITE®
Electrical field,Electronic field,Automotive sector
transparent,Flame retardant
UL
MSDS
TDS
Processing
MSDS
UL
RoHS
SVHC
PSC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | FCFC TAIWAN/AC3854 |
|---|---|---|---|
| Rockwell hardness | R 计秤, 23°C | ISO 2039-2 | 122 |
| R 级, 23°C | ASTM D785 | 122 |
| Mechanical properties | Test Condition | Test Method | FCFC TAIWAN/AC3854 |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 103 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 2160 Mpa |
| tensile strength | 23°C | ASTM D638 | 64.0 Mpa |
| optical performance | Test Condition | Test Method | FCFC TAIWAN/AC3854 |
|---|---|---|---|
| Haze ratio | 2500 µm | ASTM D1003 | < 2.0 % |
| transmissivity | 2500 µm | ASTM D1003 | > 88.0 % |
| flammability | Test Condition | Test Method | FCFC TAIWAN/AC3854 |
|---|---|---|---|
| UL flame retardant rating | 2.5 mm | UL 94 | V-0 |
| 3.0 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | FCFC TAIWAN/AC3854 |
|---|---|---|---|
| Shrinkage rate | 流动 : 3.20 mm | ASTM D955 | 0.50 - 0.70 % |
| 3.20 mm | ISO 2577 | 0.50 - 0.70 % | |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 13 g/10 min |
| Thermal performance | Test Condition | Test Method | FCFC TAIWAN/AC3854 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火, 3.18 mm，HDT | ASTM D648 | 128 °C |