PA66 Hyundai EP PA66 LD140 HYUNDAI KOREA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | HYUNDAI KOREA/Hyundai EP PA66 LD140 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 71 J/m |
| hardness | Test Condition | Test Method | HYUNDAI KOREA/Hyundai EP PA66 LD140 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 121 |
| Mechanical properties | Test Condition | Test Method | HYUNDAI KOREA/Hyundai EP PA66 LD140 |
|---|---|---|---|
| Flexural modulus | ASTM D790 | 5200 MPa | |
| tensile strength | 屈服 | ASTM D638 | 127 MPa |
| bending strength | ASTM D790 | 177 MPa |
| Electrical performance | Test Condition | Test Method | HYUNDAI KOREA/Hyundai EP PA66 LD140 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.0E+13到1.0E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 3.5 kV/mm |
| physical property | Test Condition | Test Method | HYUNDAI KOREA/Hyundai EP PA66 LD140 |
|---|---|---|---|
| density | ASTM D1505 | 1.28 g/cm³ | |
| Shrinkage rate | MD | ASTM D955 | 0.50to0.70 % |
| ash content | 20 % |
| Thermal performance | Test Condition | Test Method | HYUNDAI KOREA/Hyundai EP PA66 LD140 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 245 °C |
| melting temperature | 265 °C |