Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL1414T NA8A005TL SABIC INNOVATIVE NANSHA
LEXAN™
Electrical field、Electronic field、Household appliances、Household appliances、Bottle cap
Low temperature resistanc、transparent、Processability、Moderate liquidity、Ductility、copolymer
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414T NA8A005TL
density
ASTMD792
g/cm³
1
density
ISO1183
g/cm³
1
Melt Volume-Flow Rate (MVR)
300°C/1.2kg
ISO1133
cm3/10min
9
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
1
Shrinkage rate
MD：3.20mm
内部方法
%
0
Shrinkage rate
TD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414T NA8A005TL
Impact strength of simply supported beam gap
-30°C
ISO179/1eA
kJ/m²
6
Impact strength of simply supported beam gap
23°C
ISO179/1eA
kJ/m²
7
Tensile modulus
ASTMD638
Mpa
2
Tensile modulus
ISO527-2/1
Mpa
2
tensile strength
屈服
ASTMD638
Mpa
5
tensile strength
屈服
ISO527-2/50
Mpa
5
tensile strength
断裂
ASTMD638
Mpa
5
tensile strength
断裂
ISO527-2/50
Mpa
6
elongation
屈服
ASTMD638
%
6
elongation
屈服
ISO527-2/50
%
6
elongation
断裂
ASTMD638
%
9
elongation
断裂
ISO527-2/50
%
1
Bending modulus
50.0mm跨距
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
bending strength
屈服,50.0mm跨距
ASTMD790
Mpa
9
Bending strength 5,
ISO178
Mpa
8
Impact strength of cantilever beam gap
-30°C
ASTMD256
J/m
7
Impact strength of cantilever beam gap
23°C
ASTMD256
J/m
8
Suspended wall beam gap impact strength
-30°C
ISO180/1A
kJ/m²
6
Suspended wall beam gap impact strength
23°C
ISO180/1A
kJ/m²
7
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
7
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414T NA8A005TL
RTI Imp
UL746
°C
1
RTIElec
UL746
°C
1
RTIStr
UL746
°C
1
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
0.45MPa,Unannealed,100mmSpan
ISO75-2/Be
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,Unannealed,100mmSpan
ISO75-2/Ae
°C
1
vicat softening point
ASTMD152510
°C
1
vicat softening point
--
ISO306/B50
°C
1
vicat softening point
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
MD：23到80°C
ISO11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：23to80°C
ISO11359-2
cm/cm/°C
7
Electrical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414T NA8A005TL
Surface resistivity
ASTMD257
ohms
>
Dielectric strength
0.800mm,inOil
ASTMD149
KV/mm
1
Volume resistivity
ASTMD257
ohms·cm
>
flammability
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414T NA8A005TL
Hot filament ignition temperature
1.0mm
IEC60695-2-13
°C
8
Hot filament ignition temperature
3.0mm
IEC60695-2-13
°C
8
Burning wire flammability index
0.8mm
IEC60695-2-12
°C
8
Burning wire flammability index
1.0mm
IEC60695-2-12
°C
9