POM Homopolymer Sindustris POM N110LD Sincerity Australia Pty Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Sincerity Australia Pty Ltd./Sindustris POM N110LD |
---|---|---|---|
Impact strength of cantilever beam gap | 23°C,6.40mm | ASTM D256 | 69 J/m |
hardness | Test Condition | Test Method | Sincerity Australia Pty Ltd./Sindustris POM N110LD |
---|---|---|---|
Rockwell hardness | R级 | ASTM D785 | 82 |
Electrical performance | Test Condition | Test Method | Sincerity Australia Pty Ltd./Sindustris POM N110LD |
---|---|---|---|
Surface Resistivity | ASTM D257 | 1E+16 ohms | |
Dissipation Factor | 1MHz | ASTM D150 | 3.8E-04 |
Volume resistivity | 23°C | ASTM D257 | 1E+14 ohms·cm |
dielectric strength | 23°C,1.00mm | ASTM D149 | 24 kV/mm |
Mechanical properties | Test Condition | Test Method | Sincerity Australia Pty Ltd./Sindustris POM N110LD |
---|---|---|---|
elongation | 断裂,3.20mm | ASTM D638 | 65 % |
Flexural modulus | 6.40mm | ASTM D790 | 2550 MPa |
bending strength | 6.40mm | ASTM D790 | 89.2 MPa |
tensile strength | 屈服,3.20mm | ASTM D638 | 60.8 MPa |
flammability | Test Condition | Test Method | Sincerity Australia Pty Ltd./Sindustris POM N110LD |
---|---|---|---|
UL flame retardant rating | 0.710mm | UL 94 | HB |
3.00mm | UL 94 | HB | |
1.50mm | UL 94 | HB |
physical property | Test Condition | Test Method | Sincerity Australia Pty Ltd./Sindustris POM N110LD |
---|---|---|---|
Shrinkage rate | MD:3.20mm | ASTM D955 | 1.8to2.1 % |
density | ASTM D792 | 1.41 g/cm³ | |
melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 9.0 g/10min |
Thermal performance | Test Condition | Test Method | Sincerity Australia Pty Ltd./Sindustris POM N110LD |
---|---|---|---|
Heat distortion temperature | 0.45MPa,未退火,3.20mm,HDT | ASTM D648 | 110 °C |
1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 160 °C |