XLPE AEI SX-0620:CM601 UK AEI Compounds
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | UK AEI Compounds/AEI SX-0620:CM601 | |
|---|---|---|---|
| Tensile stress change rate | 100°C,24hr,在IRM902油中，断裂 | -13 % | |
| melt mass-flow rate | 190°C/21.6kg | 内部方法 | 2.0 g/10min |
| Tensile stress change rate | 100°C,72hr,在IRM902油中，断裂 | 2.1 % | |
| Change rate of tensile strength in air | 100°C,24hr,在IRM902油中 | 7.7 % | |
| density | BS2782620A | 1.48 g/cm³ | |
| Change rate of tensile strength in air | 120°C,168hr | IEC 60811-1-2 | 12 % |
| 70°C,168hr,在IRM903油中 | -10 % | ||
| 100°C,72hr,在IRM902油中 | 12 % | ||
| Tensile stress change rate | 120°C,168hr，断裂 | IEC 60811-1-2 | -15 % |
| Change rate of tensile strength in air | 100°C,168hr,在IRM902油中 | -6.0 % | |
| Tensile stress change rate | 70°C,168hr,在水中，断裂 | -20 % | |
| tensile strength | IEC 60811-1-1 | 10.0 MPa | |
| Change rate of tensile strength in air | 70°C,168hr,在水中 | -20 % | |
| thermosetting | Elongationunderload,20N/cm²:200°C | IEC 60811-2-1 | 60 % |
| Tensile stress change rate | 100°C,168hr,在IRM902油中，断裂 | -2.8 % | |
| HalogenAcidGasEvolution | IEC 60754-1 | <0.50 % | |
| Tensile strain | 断裂 | IEC 60811-1-1 | 170 % |
| Tensile stress change rate | 70°C,168hr,在IRM903油中，断裂 | -17 % | |
| thermosetting | Permanentelongationaftercooling | IEC 60811-2-1 | 5.0 % |
| Limiting Oxygen Index | ISO 4589-2 | 29 % |