AS(SAN) LITAC-A® 100PCF Nippon A&L Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Nippon A&L Inc./LITAC-A® 100PCF |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 1.5 kJ/m² |
| hardness | Test Condition | Test Method | Nippon A&L Inc./LITAC-A® 100PCF |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 127 |
| Mechanical properties | Test Condition | Test Method | Nippon A&L Inc./LITAC-A® 100PCF |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 3600 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 71.0 MPa |
| bending strength | 23°C | ISO 178 | 124 MPa |
| flammability | Test Condition | Test Method | Nippon A&L Inc./LITAC-A® 100PCF |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | Nippon A&L Inc./LITAC-A® 100PCF |
|---|---|---|---|
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 18.0 cm³/10min |
| density | 23°C | ISO 1183 | 1.07 g/cm³ |
| Shrinkage rate | 内部方法 | 0.20to0.50 % |
| Thermal performance | Test Condition | Test Method | Nippon A&L Inc./LITAC-A® 100PCF |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23到80°C | JISK7197 | 6E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 85.0 °C |