Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM 4102 ASAHI JAPAN
TENAC™
Automotive Applications
high strength,Aging resistance,Low gloss,Low glossiness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/4102 |
|---|---|---|---|
| melt mass-flow rate | 220℃/5kg | ISO 1133 | 15 g/10min |
| density | ISO 1183 | 1.04 g/cm |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/4102 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2250 Mpa | |
| Rockwell hardness | ISO 2039-2 | 112 R scale | |
| Tensile stress | 屈服 | ISO 527-2 | 42.0 Mpa |
| bending strength | ISO 178 | 65.0 Mpa | |
| Flexural modulus | ISO 178 | 2200 Mpa | |
| Impact strength of cantilever beam gap | ASTM D-256 | 200 J/m | |
| Charpy Notched Impact Strength | ISO 179 | 20.0 KJ/m |
| physical property | Test Condition | Test Method | ASAHI JAPAN/4102 |
|---|---|---|---|
| Shrinkage rate | Flow | ASTM D-955 | 0.40-0.60 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/4102 |
|---|---|---|---|
| vicat | ISO 306 | 98.0 °C | |
| Heat distortion temperature | 1.80MPa，未退火，HDT | ISO 75-2/A | 79.0 °C |