Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GS2010MLR MITSUBISHI THAILAND
IUPILON™ 
Camera applications
enhance、Filler: Glass fiber reinf、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI THAILAND/GS2010MLR
Impact strength of simply supported beam without notch23°CISO 17955 kJ/m²
Mechanical propertiesTest ConditionTest MethodMITSUBISHI THAILAND/GS2010MLR
bending strengthASTM D790/ISO 178105 kg/cm²(MPa)[Lb/in²]
Tensile modulusISO 527-24500 Mpa
Flexural modulusASTM D790/ISO 1782800 kg/cm²(MPa)[Lb/in²]
bending strengthISO 178135 Mpa
Tensile strain断裂ISO 527-22.9 %
Flexural modulusISO 1784000 Mpa
Tensile modulusASTM D638/ISO 5273300 kg/cm²(MPa)[Lb/in²]
tensile strength 断裂ISO 527-278.0 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI THAILAND/GS2010MLR
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 4
otherTest ConditionTest MethodMITSUBISHI THAILAND/GS2010MLR
characteristic玻纤增强
purpose相机应用
Physical propertiesTest ConditionTest MethodMITSUBISHI THAILAND/GS2010MLR
densityASTM D792/ISO 11831.27
flammabilityTest ConditionTest MethodMITSUBISHI THAILAND/GS2010MLR
UL flame retardant rating0.75mmUL 94V-0
physical property Test ConditionTest MethodMITSUBISHI THAILAND/GS2010MLR
Shrinkage rateTD:3.20mm0.40-0.60 %
Melt volume flow rate300°C/1.2kgISO 11339.00 cm3/10min
Shrinkage rateMD:3.20mm0.30-0.50 %
Water absorption rate饱和,23°CISO 620.14 %
melt mass-flow rate300°C/1.2kgISO 113310 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI THAILAND/GS2010MLR
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B145 °C
1.8MPa,未退火，HDTISO 75-2/A140 °C
Linear coefficient of thermal expansionMDISO 11359-24E-05 cm/cm/°C
TDISO 11359-26.7E-05 cm/cm/°C