PC/ABS NX10302 SABIC INNOVATIVE NANSHA
LNP™ THERMOCOMP™
Casters,Electrical applications
High mobility,Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/NX10302 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 悬壁梁无缺口冲击强度 | ASTM D4812 | NB J/m |
| tensile strength | 5mm/min，23°C | ASTM D638 | 47.0 Mpa |
| elongation at break | 屈服，5mm/min，23°C | ASTM D638 | 4.2 % |
| 5mm/min，23°C | ASTM D638 | 100 % | |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 600 J/m |
| bending strength | 1.3mm/min，23°C | ASTM D790 | 79.0 Mpa |
| Tensile modulus | 50mm/min，23°C | ASTM D638 | 2480 Mpa |
| tensile strength | 屈服，5mm/min，23°C | ASTM D638 | 46.0 Mpa |
| bending strength | 屈服，1.3mm/min，23°C | ASTM D790 | 80.0 Mpa |
| Flexural modulus | 1.3mm/min，23°C | ASTM D790 | 2400 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/NX10302 |
|---|---|---|---|
| Shrinkage rate | MD3.20mm | ASTM D995 | 0.60-0.65 % |
| Water absorption rate | 吸湿性 | ASTM D570 | 0.0200 % |
| Shrinkage rate | TD3.20mm | ASTM D995 | 0.50-0.56 % |
| Water absorption rate | (23°C,24hr) | ASTM D570 | 0.010 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/NX10302 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD | ASTM D696 | 9.1E-05 cm/cm/°C |
| Heat distortion temperature | 1.80MPa未退火，HDT | ASTM D648 | 108 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 8.47E-05 cm/cm/°C |