Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PET HX7509HP SABIC INNOVATIVE US
XYLEX™
Automotive Applications、Electronic and electrical
Flame retardant、High heat resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HX7509HP |
|---|---|---|---|
| Thermal Conductivity | ISO8302 | 0.23 W/m/K | |
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831 | 1E-04 cm/cm/°C |
| Vicat Softening Temperature | -- | ISO306/B50 | 125 °C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 119 °C |
| Linear thermal expansion coefficient | MD:-40到40°C | ISO11359-2 | 6.8E-05 cm/cm/°C |
| Vicat Softening Temperature | -- | ASTM D-596 | 126 °C |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 106 °C |
| Linear thermal expansion coefficient | TD:-40到40°C | ASTME831 | 1E-04 cm/cm/°C |
| ISO11359-2 | 6.8E-05 cm/cm/°C | ||
| Heat Deflection Temperature | 1.8MPa,未退火,64.0mm跨距10 | ISO75-2/Af | 108 °C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/HX7509HP |
|---|---|---|---|
| Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.40到0.60 % |
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.050 % |
| Melt Mass-Flow Rate | 265°C/2.16kg | ASTMD1238 | 12 g/10min |
| Modeling Shrinkage | TD:3.20mm | 内部方法 | 0.50到0.70 % |
| Melt Volume flow Rate | 265°C/2.16kg | ISO1133 | 11.5 cm3/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.12 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HX7509HP |
|---|---|---|---|
| Tensile Strength | 断裂 | ISO527-2/50 | 62.0 Mpa |
| Tensile Modulus | --3 | ASTMD638 | 2150 Mpa |
| Tensile Elongation | 断裂4 | 140 % | |
| Tensile Strength | 63.0 Mpa | ||
| Tensile Elongation | 断裂 | ISO527-2/50 | 130 % |
| Flexural Stress | 屈服,50.0mm跨距5 | ASTMD790 | 95.0 Mpa |
| --6,7 | ISO178 | 92.0 Mpa | |
| Flexural Modulus | 50.0mm跨距5 | ASTMD790 | 2300 Mpa |
| Tensile Strength | 屈服 | ISO527-2/50 | 60.0 Mpa |
| Tensile Modulus | -- | ISO527-2/1 | 2300 Mpa |
| Tensile Elongation | 屈服 | ISO527-2/50 | 5.8 % |
| 屈服4 | ASTMD638 | 6.3 % | |
| Tensile Strength | 60.0 Mpa | ||
| Flexural Modulus | --6 | ISO178 | 2260 Mpa |
| Optical | Test Condition | Test Method | SABIC INNOVATIVE US/HX7509HP |
|---|---|---|---|
| Transmittance | 2540µm | ASTMD1003 | 88.0 % |
| Haze | 2.0 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HX7509HP |
|---|---|---|---|
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 77.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 10 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/HX7509HP |
|---|---|---|---|
| Flame Rating | 0.75mm | UL94 | V-2 |