| Impact resistance | Test Condition | Test Method | FCFC TAIWAN/AG15E1 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C, 6.35 mm | ASTM D256 | 140 J/m |
| hardness | Test Condition | Test Method | FCFC TAIWAN/AG15E1 |
|---|---|---|---|
| Rockwell hardness | R 计秤, 23°C | ISO 2039-2 | 110 |
| R 级, 23°C | ASTM D785 | 110 |
| Mechanical properties | Test Condition | Test Method | FCFC TAIWAN/AG15E1 |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 86.0 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 2750 Mpa |
| tensile strength | 23°C | ASTM D638 | 48.0 Mpa |
| flammability | Test Condition | Test Method | FCFC TAIWAN/AG15E1 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | FCFC TAIWAN/AG15E1 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.05 g/cm³ |
| melt mass-flow rate | 220°C/10.0 kg | ASTM D1238 | 20 g/10 min |
| density | -- | ASTM D792 | 1.05 g/cm³ |
| melt mass-flow rate | 200°C/5.0 kg | ASTM D1238 | 1.8 g/10 min |
| Thermal performance | Test Condition | Test Method | FCFC TAIWAN/AG15E1 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 退火3，HDT | ASTM D648 | 100 °C |
| vicat | ISO 306/A | 103 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 12.7 mm，HDT | ASTM D648 | 86.0 °C |
| injection | Test Condition | Test Method | FCFC TAIWAN/AG15E1 |
|---|---|---|---|
| drying time | 2.0 to 3.0 hr | ||
| Injection Pressure | 68.6 to 108 Mpa | ||
| Processing (melt) temperature | 190 to 230 °C | ||
| drying temperature | 70 to 80 °C | ||
| Temperature | 40 to 80 °C |