Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT BM6450XD BK560 DUPONT USA
Cristin®
Blow molding applications
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | DUPONT USA/BM6450XD BK560 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 80.0 °C |
| 1.8MPa,未退火 | ISO75-2/A | 50.0 °C | |
| Melting Temperature | ISO11357-3 | 220 °C | |
| Heat Deflection Temperature | 0.45MPa,退火 | ISO75-2/B | 130 °C |
| -，0.45 Mpa，未退火（Flatwise） | ISO 75B-1, -2 | 130 ℃ |
| Physical | Test Condition | Test Method | DUPONT USA/BM6450XD BK560 |
|---|---|---|---|
| SpecificHeatCapacityofMelt | 2210 J/kg/°C | ||
| ThermalConductivityofMelt | 0.15 W/m/K | ||
| MediumDensity | 1.03 g/cm³ | ||
| Modeling Shrinkage | TD | ISO294-4 | 1.7 % |
| MD | 1.5 % |
| Mechanical Properties | Test Condition | Test Method | DUPONT USA/BM6450XD BK560 |
|---|---|---|---|
| Tensile Modulus | 23 ℃, 1.0 mm/min | ISO 527-1, -2 | 1600 MPa |
| Flexural Strength | ASTM D790/ISO 178 | 50 kg/cm²(MPa)[Lb/in²] | |
| Tensile Strain | 屈服 | ISO527-2 | 9.0 % |
| Tensile Stress | 34.0 Mpa | ||
| Tensile Modulus | ASTM D638/ISO 527 | 1600 kg/cm²(MPa)[Lb/in²] | |
| Tensile Strain (Yield) | 23 °C, 50 mm/min | ISO 527-1, -2 | 9.3 % |
| Flexural Modulus | ISO178 | 1600 Mpa | |
| 23℃, 2 mm/min | ISO 178 | 1600 MPa | |
| Tensile Stress (Yield) | 23 ℃, 50 mm/min | ISO 527-1, -2 | 34 MPa |
| Charpy Unnotched Impact Strength | -，23 ℃, Type 1, Edgewise | ISO 179 | No Break KJ/m |
| Nominal Tensile Strain at Break | ISO527-2 | >50 % | |
| Flexural Stress | ISO178 | 50.0 Mpa | |
| Tensile Modulus | ISO527-2 | 1600 Mpa | |
| Charpy Unnotched Impact Strength | -，-30 ℃, Type 1, Edgewise | ISO 179 | No Break KJ/m |
| Flexural Modulus | ASTM D790/ISO 178 | 1600 kg/cm²(MPa)[Lb/in²] |
| Other | Test Condition | Test Method | DUPONT USA/BM6450XD BK560 |
|---|---|---|---|
| purpose | 吹塑成型应用 | ||
| characteristic | 可加工性良好 耐化学性良好 |
| Impact Properties | Test Condition | Test Method | DUPONT USA/BM6450XD BK560 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak |
| 23°C | NoBreak |
| Physical Properties | Test Condition | Test Method | DUPONT USA/BM6450XD BK560 |
|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1.21 |
| Flammability | Test Condition | Test Method | DUPONT USA/BM6450XD BK560 |
|---|---|---|---|
| Burning Rate | 1.00mm | ISO3795 | 40 mm/min |
| FMVSS Flammability | FMVSS302 | B |
| Electrical Properties | Test Condition | Test Method | DUPONT USA/BM6450XD BK560 |
|---|---|---|---|
| Dielectric Strength | IEC60243-1 | 31 KV/mm | |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Surface Resistivity | >1.0E+15 ohms | ||
| Dissipation Factor? | 1MHz | IEC60250 | 0.020 |
| 100Hz | 7E-03 |
| Processing | Test Condition | Test Method | DUPONT USA/BM6450XD BK560 |
|---|---|---|---|
| Mold Temperature | 30-130 °C |