Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT UT6005 901510 COVESTRO GERMANY
Makroblend®
electrical equipment、transport、electronic product、Communication Application
Low temperature resistanc、Creep resistance、Resistance to stress crac
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | COVESTRO GERMANY/UT6005 901510 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Multi axis Instrumented Impact Energy | -30°C | ISO 6603-2 | 58.0 J |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Suspended wall beam without notch impact strength | -30°C | ISO 180 | NoBreak |
| Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 47.0 J |
| Multi axis Instrumented Peak Impact Force | 23°C | ISO 6603-2 | 3800 N |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | NoBreak |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO 6603-2 | 5000 N |
| hardness | Test Condition | Test Method | COVESTRO GERMANY/UT6005 901510 |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 108 Mpa |
| Electrical performance | Test Condition | Test Method | COVESTRO GERMANY/UT6005 901510 |
|---|---|---|---|
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 30 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案B | IEC 60112 | V |
| relative permittivity | 23°C,1MHz | IEC 60250 | 3.00 |
| Volume resistivity | 23°C | IEC 60093 | >1.0E+17 ohms·cm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 3.20 |
| Surface Resistivity | IEC 60093 | >1.0E+17 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 7E-04 |
| 23°C,1MHz | IEC 60250 | 4.5E-03 |
| Mechanical properties | Test Condition | Test Method | COVESTRO GERMANY/UT6005 901510 |
|---|---|---|---|
| bending strength | 3.5%Strain,23°C | ISO 178 | 70.0 Mpa |
| Bending Strain | 23°C | ISO 178 | 6.0 % |
| tensile strength | 屈服,23°C | ISO 527-2/50 | 60.0 Mpa |
| 断裂,23°C | ISO 527-2/50 | 50.0 Mpa | |
| bending strength | 23°C | ISO 178 | 80.0 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 5.0 % |
| Flexural modulus | 23°C | ISO 178 | 2150 Mpa |
| Tensile modulus | 23°C | ISO 527-2/1 | 2200 Mpa |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | >50 % |
| flammability | Test Condition | Test Method | COVESTRO GERMANY/UT6005 901510 |
|---|---|---|---|
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 750 °C |
| Limiting Oxygen Index | ISO 4589-2 | 21 % | |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | COVESTRO GERMANY/UT6005 901510 |
|---|---|---|---|
| Shrinkage rate | TD2 | ISO 2577 | 0.70-0.90 % |
| Apparent density | ISO 60 | 0.65 g/cm³ | |
| Shrinkage rate | TD:90°C,1hr | ISO 2577 | 0.10-0.20 % |
| MD2 | ISO 2577 | 0.70-0.90 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.50 % | |
| Shrinkage rate | MD:90°C,1hr | ISO 2577 | 0.10-0.20 % |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 18.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | COVESTRO GERMANY/UT6005 901510 |
|---|---|---|---|
| vicat | ISO 306/B120 | 126 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 110 °C |
| thermal conductivity | 23°C | ISO 8302 | 0.20 W/m/K |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 85.0 °C |