PBT 420-7001 SABIC INNOVATIVE THAILAND
VALOX™
Lawn equipment、Garden equipment、Industrial applications、Automotive External Parts、Electrical field、Electronic field、Architectural application、Outdoor applications、Electrical appliances、Engine hood parts、Medical supplies、Nursing supplies、Plastic bag、Automotive interior parts、Casters、Household goods、Petroleum Applications、Natural gas supplies、sporting goods、Textile application、Lighting applications
Glass fiber reinforced、dimensional stability 、High rigidity、high strength、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420-7001 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 45 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 80 J/m |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 45 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 45 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420-7001 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 9300 Mpa | |
| tensile strength | Yield | ASTM D638 | 120 Mpa |
| 断裂 | ISO 527-2/5 | 125 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/5 | 2.0 % |
| bending strength | Break,50.0mmSpan | ASTM D790 | 190 Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 19.0 mg |
| Flexural modulus | 50.0mmSpan | ASTM D790 | 7580 Mpa |
| Tensile strain | Break | ASTM D638 | 2.7 % |
| Tensile modulus | ASTM D638 | 9300 Mpa | |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 195 Mpa |
| tensile strength | Break | ASTM D638 | 120 Mpa |
| Tensile strain | Yield | ASTM D638 | 2.7 % |
| bending strength | ISO 178 | 195 Mpa | |
| Flexural modulus | ISO 178 | 8500 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420-7001 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.30-0.80 % |
| TD：--2 | 内部方法 | 0.50-1.0 % | |
| melt mass-flow rate | 250°C/2.16kg | ISO 1133 | 17 g/10min |
| Shrinkage rate | TD：--3 | 内部方法 | 0.40-0.60 % |
| Water absorption rate | 24hr | ASTM D570 | 0.090 % |
| Shrinkage rate | TD：--5 | 内部方法 | 0.60-0.90 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.080 % |
| Shrinkage rate | MD：--2 | 内部方法 | 0.30-0.70 % |
| density | ASTM D792 | 1.53 g/cm³ | |
| Specific volume | ASTM D792 | 0.660 cm³/g | |
| Shrinkage rate | MD：--3 | 内部方法 | 0.30-0.50 % |
| MD：--4 | 内部方法 | 0.50-0.80 % |